Chemical Composition of SS Buttweld Fittings
Grade C Mn Si P S Cr Ni
SS 304 0.08 max 2 max 0.75 max 0.045 max 0.030 max 18 – 20 8 – 11
Grade C Mn Si P S Cr Ni
SS 304L 0.035 max 2.0 max 1.0 max 0.045 max 0.03 max 18 – 20 8 – 13
Grade C Si P Mn Mo Ni S Cr N
SS 304H 0.10 max 0.75 max 0.045 max 2 max – 8 – 10.5 0.03 max 18 – 20 –
Grade C Mn Si P S Cr Mo Ni Fe
SS 310S 0.08 max 2.0 max 1.00 max 0.045 max 0.030 max 24.00 – 26.00 0.75 max 19.00 – 21.00 53.095 min
SS 310 0.015 max 2.0 max 0.15 max 0.020 max 0.015 max 24.00 – 26.00 0.10 max 19.00 – 21.00 54.7 min
Grade C Mn P Si Ni Fe S Cr Mo
SS 316L 0.035 max 2.0 max 0.045 max 1.0 max 10.00 – 14.00 68.89 min 0.030 max 16.00 – 18.00 2.00 – 3.00
SS 316 0.08 max 2.0 max 0.045 max 1.0 max 11.00 – 14.00 67.845 min 0.030 max 16.00 – 18.00 2.00 – 3.00
Grade C Mn P S Si Cr Ni Mo Fe
SS 316Ti 0.08 max 2.0 max 0.045 max 0.030 max 0.75 max 16.00 – 18.00 10.00 – 14.00 2.00 – 3.00 68.395 min
Grade C Si Mn P Ni Fe S Cr Mo
SS 317 0.08 max 1.0 max 2.0 max 0.045 max 11.00 – 15.00 57.845 min 0.030 max 18.00 – 20.00 3.00 – 4.00
Grade C Mn S Cr Si P Mo Ni Fe
SS 317L 0.035 max 2.0 max 0.030 max 18.00 – 20.00 1.0 max 0.045 max 3.00 – 4.00 11.00 – 15.00 57.89 min
Grade C Mn Cr Cb Si P S Ni Fe
SS 347H 0.04 – 0.10 2.0 max 17.00 – 19.00 8xC – 1.10 1.0 max 0.045 max 0.030 max 9.0 -13.0 63.72 min
SS 347 0.08 max 2.0 max 17.00 – 20.00 10xC – 1.10 1.0 max 0.045 max 0.030 max 9.00 – 13.00 62.74 min
Grade C P S Mn Si Cr Mo Ni N
410 min. – – – – – 11.5 – – –
max. 0.15 0.040 0.030 1.0 1.00 13.5 – 0.75 –
Grade C Mn S Cr Mo Si P Ni N Fe
SS 446 0.2 max 1.5 max 0.030 max 23 – 30 – 0.75 max 0.04 max 0.50 max 0.10 – 0.25 Balance
Grade C Mn P S Si Cr MO Ni N
446 Min – – – – – 23.00 – – 0.10
max 0.2 1.5 0.75 0.030 30.00 0.040 – 0.50 0.25 –
Grade C S Cr Mn Si Ni Cu P Mo
SS 904L 0.020 max 0.030 max 19.00 – 23.00 2.00 max 1.00 max 23.00 – 28.00 1.00 – 2.00 0.040 max 4.00 – 5.00 max

Mechanical Properties of SS Butt weld Pipe Fittings
Grade Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
304 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %

Grade Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
304L 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %

Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
304h 8.0 g/cm3 Psi – 75000 , MPa – 515 1400 °C (2550 °F) Psi – 30000 , MPa – 205 40 %
Grade Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
310/310s 7.9 g/cm3 1402 °C (2555 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40 %
Grade Melting Point Density Elongation Tensile Strength Yield Strength (0.2%Offset)
SS 316L 1399 °C (2550 °F) 8.0 g/cm3 35 % Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205
SS 316 1400 °C (2550 °F) 8.0 g/cm3 35 % Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205
Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
316Ti 8.0 g/cm3 Psi – 75000 , MPa – 515 1399 °C (2550 °F) Psi – 30000 , MPa – 205 35 %
Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
317 7.9 g/cm3 Psi – 75000 , MPa – 515 1400 °C (2550 °F) Psi – 30000 , MPa – 205 35 %
Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
317L 7.9 g/cm3 Psi – 75000 , MPa – 515 1400 °C (2550 °F) Psi – 30000 , MPa – 205 35 %
Grade Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
347/347h 8.0 g/cm3 1454 °C (2650 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
Grade Density Melting Point Yield Strength (0.2%Offset) Tensile Strength Elongation
446 7.5 g/cm3 1510 °C (2750 °F) Psi – 40,000 , MPa – 275 Psi – 75,000 , MPa – 485 20 %
Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
446 7.5 g/cm3 Psi – 75,000 , MPa – 485 1510 °C (2750 °F) Psi – 40,000 , MPa – 275 20 %
Grade Density Tensile Strength Melting Point Yield Strength (0.2%Offset) Elongation
904L 7.95 g/cm3 Psi – 71000 , MPa – 490 1350 °C (2460 °F) Psi – 32000 , MPa – 220 35 %